SabikUltem 2210EPRresin adalah20% Serat Kaca diisi, Polyimide aliran tinggi (Tg 217C) dengan pelepasan cetakan internal dan peningkatan elektroplatability.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 137 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 137 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6890 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 206 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 206 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6890 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 6890 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 587 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 14 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 210 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 211 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 206 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 213 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 208 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 105 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 105 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 105 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.39 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 13 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 1 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.4 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:04/30/2002 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/30/2002 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |