SabikUltem EXUM0198resin adalahResin Thermoplastic Polyimide Extem* XH1015.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 103 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 10 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3420 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 168 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3130 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 0 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 0 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 0 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 0 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 43 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 1390 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 0 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 260 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 250 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 235 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 237 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 5.E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C sampai 150°C, xflow | 5.1E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/120 | 0 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 0 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | Satu, satu.2 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 10 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 2.3 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.6 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 0 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:03/30/2007 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 380 - 405 | °C |
| Suhu Nozzle | 375 - 400 | °C |
| Suhu depan - Zona 3 | 380 - 405 | °C |
| Tengah - Zona 2 Suhu | 370 - 395 | °C |
| Bagian belakang - Zona 1 Suhu | 360 - 380 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:03/30/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem EXUM0198.pdf |
|