SabikUltem EXUM0169resin adalahPeningkatan fleksibilitas, transparansi, peningkatan aliran campuran Polyimide (Tg 200C) dengan pelepasan cetakan internal dan peningkatan fleksibilitas.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 103 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 85 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 80 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3210 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 145 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3320 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 108 | - | ASTM D 785 |
| Tekanan tarik, hasil, 5 mm/menit | 98 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 80 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 135 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Impact, tidak diukir, -30°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 35 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 2085 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 48 | J | ASTM D 3763 |
| Energi Total Dampak Instrumen, -20°C | 8 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 2 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 2 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 2 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 192 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 173 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 178 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 150°C, aliran | 5.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 192 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 195 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 168 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 43 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.36 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 56 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+17 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.6E+17 | Ohm | ASTM D 257 |
| Faktor Dissipasi, 1 MHz | 0.0061 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:06/02/2006 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 330 - 355 | °C |
| Suhu Nozzle | 325 - 350 | °C |
| Suhu depan - Zona 3 | 330 - 355 | °C |
| Tengah - Zona 2 Suhu | 320 - 345 | °C |
| Bagian belakang - Zona 1 Suhu | 310 - 330 | °C |
| Suhu Cetakan | 95 - 135 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:06/02/2006 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem EXUM0169.pdf |
|