SabikUltem DU319resin adalahCampuran Polyetherimide transparan. ECO Conform. US FDA dan EU Food Contact Compliant dalam warna yang diakui.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 82 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 60 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3370 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 165 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 110 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 75 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 36 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 155 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 26 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 950 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 40 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 181 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 165 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.86E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 177 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 180 | °C | ISO 306 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.29 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm (5) | 0.6 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 295°C/6,6 kgf | 8.1 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.17 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/11/09 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 - 8 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 300 - 330 | °C |
| Suhu Nozzle | 300 - 330 | °C |
| Suhu depan - Zona 3 | 295 - 325 | °C |
| Tengah - Zona 2 Suhu | 290 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 315 | °C |
| Suhu Cetakan | 95 - 150 | °C |
| Tekanan Belakang | 0.7 - 1.4 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:2009/11/09 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |