SabikUltem DH1004resin adalah...
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 95 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 90 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 85 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2900 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 140 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3000 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 97 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 80 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 136 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 70 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 3300 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 88 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, 0°C | 99 | J | ASTM D 3763 |
| Energi Total Dampak Instrumen, -20°C | 88 | J | ASTM D 3763 |
| Duktilitas Dampak Instrumen, 23°C | 100 | % | ASTM D 3763 |
| Duktilitas Dampak Instrumen, 0°C | 100 | % | ASTM D 3763 |
| Duktilitas Dampak Instrumen, -20°C | 90 | % | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 11 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 214 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 204 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 5.6E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C sampai 150°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.19 | W/m-°C | ASTM C 177 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat A/50 | 219 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 10 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 14 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Indeks Oksigen (LOI) | 46 | % | ASTM D 2863 |
| Densitas Asap, Api, Ds 4 min | 0.7 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:10/16/2008 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 6 - 8 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 355 - 390 | °C |
| Suhu Nozzle | 345 - 390 | °C |
| Suhu depan - Zona 3 | 345 - 390 | °C |
| Tengah - Zona 2 Suhu | 335 - 390 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 390 | °C |
| Suhu Cetakan | 130 - 160 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:10/16/2008 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem DH1004.pdf |
|