SabikUltem D9065resin adalahCampuran polietherimide. memenuhi FAR 25.853 dan OSU 65/65 dengan toksisitas rendah, asap, dan evolusi api.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 88 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 88 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3100 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 124 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3100 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 149 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 96 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 2029 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 67 | J | ASTM D 3763 |
| Energi dampak instrumen @ puncak, -30 | 58 | J | ASTM D 3763 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.32 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 15.6 | g/10 menit | ASTM D 1238 |
| Karakteristik Api | Nilai | Satuan | Standar |
| OSU total pelepasan panas (tes 2 menit) | 10 | kW-menit/m2 | FAR 25.853 |
| Kecepatan pelepasan panas puncak OSU (tes 5 menit) | 50 | kW/m2 | FAR 25.853 |
| Sumber GMD, terakhir diperbarui:01/13/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 340 - 360 | °C |
| Suhu Nozzle | 330 - 355 | °C |
| Suhu depan - Zona 3 | 340 - 360 | °C |
| Tengah - Zona 2 Suhu | 325 - 350 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 340 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/13/2000 |
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem D9065.pdf |
|