SabikUltem CRS5011resin adalahTransparan, Enhanced flow Polyetherimide copolymer (Tg 225C) dengan peningkatan ketahanan kimia terhadap asam kuat, basa, aromatik, dan keton.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 99 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2890 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 137 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3100 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 58 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 2082 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 204 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 160 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 155 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 160 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 11 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.2 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0021 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.47 | mm | UL 94 |
| CSA (Lihat File untuk daftar lengkap) | LS88480 | File No. | CSA terdaftar |
| Sumber GMD, terakhir diperbarui:01/13/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 365 - 390 | °C |
| Suhu Nozzle | 360 - 380 | °C |
| Suhu depan - Zona 3 | 365 - 390 | °C |
| Tengah - Zona 2 Suhu | 355 - 375 | °C |
| Bagian belakang - Zona 1 Suhu | 345 - 365 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/13/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem CRS5011.pdf |
|