SabikXenoy1402Bresin adalahBlowmouldable, paduan PC / poliester yang tidak diperkuat.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 68 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1990 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 694 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 534 | J/m | ASTM D 256 |
| Gardner yang dimodifikasi, 23°C | 44 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 96 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Volume Spesifik | 0.84 | cm3/g | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.9 - 1.1 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.9 - 1.1 | % | Metode S-Plastics |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 95 - 100 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.01 - 0.02 | % |
| Kandungan Kelembaban Minimal | 0.02 | % |
| Suhu Peleburan (Parison) | 240 - 250 | °C |
| Barel - Zona 1 Suhu | 235 - 245 | °C |
| Barel - Zona 2 Suhu | 235 - 245 | °C |
| Barel - Zona 3 Suhu | 235 - 245 | °C |
| Barel - Zona 4 Suhu | 235 - 245 | °C |
| Adaptor - Zona 5 Suhu | 235 - 245 | °C |
| Kepala - Zona 6 - Suhu puncak | 235 - 245 | °C |
| Kepala - Zona 7 - Suhu bawah | 235 - 245 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Suhu mati | 240 - 250 | °C |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||