SabikCycoloy MC8234resin adalahPC + ABS, tahan api tanpa klorinasi atau brominasi aditif. ketahanan panas tinggi, direkomendasikan untuk aplikasi dinding tipis.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 40 | % | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 2580 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 121 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 453 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 54 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 112 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 87 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 101 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 93 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 7.2E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 7.2E-05 | 1/°C | ASTM D 696 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
| Indeks suhu relatif, Elec | 85 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 85 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 85 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.1 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.4 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/2,16 kgf | 22 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.6E+17 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.E+16 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 24.3 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 2.8 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.7 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0052 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.0071 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-2 Flame Class Rating (3) | 0.76 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.49 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3.4 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 2.48 | mm | UL 94 |
| CSA (Lihat File untuk daftar lengkap) | LS88480 | File No. | CSA terdaftar |
| Indeks Oksigen (LOI) | 30 | % | ASTM D 2863 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 80 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 230 - 265 | °C |
| Suhu Nozzle | 230 - 265 | °C |
| Suhu depan - Zona 3 | 230 - 265 | °C |
| Tengah - Zona 2 Suhu | 225 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 250 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Cycoloy MC8234.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|