SabikCycoloy XCY480resin adalahAliran tinggi
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2270 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2270 | MPa | ASTM D 638 |
| Tekanan Fleksural | 73 | MPa | ASTM D 790 |
| Modulus Flexural | 2140 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 43 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2150 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 47 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 560 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, 0°C | 450 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 260 | J/m | ASTM D 256 |
| Dampak Multiaxial | 130 | J | ISO 6603 |
| Izod Impact, bernotas 80*10*3 +23°C | 55 | kJ/m2 | ISO 180/1A |
| Izod Dampak, bertanda 80*10*3 0°C | 46 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 19 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 55 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 20 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 117 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 95 | °C | ASTM D 648 |
| CTE, -30°C sampai 80°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C sampai 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat A/50 | 129 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 118 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 118 | °C | ISO 75/Be |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 35 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.13 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.47 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/2,16 kg | 12 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 31 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/02/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 240 - 270 | °C |
| Suhu Nozzle | 220 - 260 | °C |
| Suhu depan - Zona 3 | 230 - 270 | °C |
| Tengah - Zona 2 Suhu | 230 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 210 - 240 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:04/02/2008 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Cycoloy XCY480.pdf |
|