SabikCycoloy LG9020resin adalahLow Gloss Cycoloy. Tersedia hanya dalam alami, untuk menjadi warna khusus terkonsentrasi dan UV stabil di percetakan cetakan.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 54 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 120 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2280 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2280 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 53 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 52 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4.3 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 120 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2390 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 83 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 645 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 385 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 57 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 54 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 32 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 63 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 123 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 126 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 103 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 123 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 125 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 101 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.13 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 18 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.13 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.39 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.12 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 20 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/25/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 240 - 290 | °C |
| Suhu Nozzle | 240 - 290 | °C |
| Suhu depan - Zona 3 | 240 - 290 | °C |
| Tengah - Zona 2 Suhu | 240 - 285 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 275 | °C |
| Suhu Hopper | 60 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/25/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |