SabikCycoloy HC1204HLresin adalahPerpaduan PC/ABS Untuk perangkat medis dan aplikasi farmasi Manajemen perubahan perawatan kesehatan, biokompatibel
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 57 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 47 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, aliran | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 126 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 128 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 102 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.6 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 22 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:09/18/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 110 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 240 - 280 | °C |
| Suhu depan - Zona 3 | 250 - 290 | °C |
| Tengah - Zona 2 Suhu | 250 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:09/18/2007 | ||
Untuk informasi lebih lanjut silahkan unduh lembar data | |
 | S-Plastics Cycoloy HC1204HL.pdf |