SabikCycoloy EXCY0236resin
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 57 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | > 50 | % | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Kekerasan, Rockwell L | 100 | - | ISO 2039-2 |
| Kekerasan, Rockwell R | 120 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Dampak Multiaxial | 90 | J | ISO 6603 |
| Izod Impact, bernotas 80*10*3 +23°C | 50 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 30 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 30 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Panas spesifik | 2.6 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.18 | W/m-°C | ISO 8302 |
| CTE, -40°C sampai 40°C, aliran | 7.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.9E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Uji tekanan bola, perkiraan maksimum | 125 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 135 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 139 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 128 | °C | ISO 75/Be |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 27 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 51 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.1 | - | IEC 60250 |
| Permittivitas relatif, 1 kHz | 3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.04 | - | IEC 60250 |
| Faktor Dissipasi, 1 kHz | 0.004 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.009 | - | IEC 60250 |
| Sumber GMD, terakhir diperbarui:08/26/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 110 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 240 - 280 | °C |
| Suhu depan - Zona 3 | 250 - 290 | °C |
| Tengah - Zona 2 Suhu | 250 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:08/26/2008 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy EXCY0236.pdf |
|