SabikCycoloy EXCY0223resin
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 46 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3550 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 98 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3550 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Dampak Multiaxial | 80 | J | ISO 6603 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/120 | 132 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 16 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Densitas asap NBS, berapi, 4 menit (3,2 mm) | 130 | - | ASTM E 662 |
| Densitas asap NBS, berapi, 20 menit (3,2 mm) | 330 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:09/12/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 300 | °C |
| Suhu Nozzle | 230 - 290 | °C |
| Suhu depan - Zona 3 | 240 - 300 | °C |
| Tengah - Zona 2 Suhu | 230 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 210 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:09/12/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy EXCY0223.pdf |
|