SabikCycoloy EXCY0175resin adalahcampuran PC+ABS tujuan umum yang dikembangkan khusus untuk aplikasi yang membutuhkan kekuatan jalur las, aliran/panas tinggi dengan dampak yang sangat baik dan ductility suhu rendah.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | > 50 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2300 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 60 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Kekerasan, Rockwell L | 95 | - | ISO 2039-2 |
| Kekerasan, Rockwell R | 120 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 550 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 300 | J/m | ASTM D 256 |
| Izod Dampak, pintu ganda, 23°C | 150 | J/m | Metode S-Plastics |
| Dampak Multiaxial | 115 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 65 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 65 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 25 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 25 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 130 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 108 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM E 1530 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 130 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 132 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 122 | °C | ISO 75/Be |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 108 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.15 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 19 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.4 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 18 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Permittivitas relatif, 1 kHz | 3 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | ASTM D 150 |
| Faktor Dissipasi, 1 kHz | 0.0073 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | ASTM D 150 |
| Permittivitas relatif, 1,2 GHz | 2.7 | - | ASTM D 2520 - Mth B |
| Resistivitas Volume | > 1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | > 1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 45 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik dalam minyak, 1,5 mm | 30 | kV/mm | IEC 60243-1 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.8 | mm | UL 94 |
| UL Diakui, 94HB Kelas Api Nilai ke-2 (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 650°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:12/19/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 110 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 240 - 280 | °C |
| Suhu depan - Zona 3 | 250 - 290 | °C |
| Tengah - Zona 2 Suhu | 250 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:12/19/2006 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy EXCY0175.pdf |
|