SabikCycoloy EXCY0109resin adalahPC + ABS Campuran dengan peningkatan ketahanan kimia.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 52 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2000 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 74 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*3 +23°C | 40 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/120 | 117 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 90 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.21 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 9 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:05/04/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 110 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 240 - 280 | °C |
| Suhu depan - Zona 3 | 250 - 290 | °C |
| Tengah - Zona 2 Suhu | 250 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:05/04/2005 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy EXCY0109.pdf |
|