SabikCycoloy EXCY0102resin adalahPerpaduan PC yang dimodifikasi menawarkan tampilan logam dengan visibilitas aliran minimal.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 61 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | > 90 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2400 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 61 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 59 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 100 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 70 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 37 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 134 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 106 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.22 | W/m-°C | ASTM E 1530 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 134 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 136 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.16 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 14 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.16 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.6 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 11 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.E+15 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 26 | kV/mm | ASTM D 149 |
| Permittivitas Relatif, 1 MHz | 2.8 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.007 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:03/09/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 300 - 320 | °C |
| Suhu Nozzle | 300 - 320 | °C |
| Suhu depan - Zona 3 | 300 - 320 | °C |
| Tengah - Zona 2 Suhu | 285 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 290 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:03/09/2005 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy EXCY0102.pdf |
|