SabikCycoloy EXCY0052resin adalahHeat Stabilized, Impact Modified, PC+ABS, untuk film SLX Tie layer
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 52 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2170 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2350 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 650 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 103 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.14 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 8.1 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:03/23/2004 | |||
| Parameter | ||
| Ekstrusi Film | Nilai | Satuan |
| Suhu Pengeringan | 90 - 110 | °C |
| Waktu Pengeringan | 4 | jam |
| Waktu pengeringan (kumulatif) | 6 - 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Barel - Belakang | 220 - 250 | °C |
| Suhu Barel - Rata-rata | 220 - 250 | °C |
| Suhu Barel - Depan | 220 - 250 | °C |
| Suhu mati | 220 - 250 | °C |
| Suhu gulungan | 200 - 250 | °C |
| Sumber GMD, terakhir diperbarui:03/23/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy EXCY0076.pdf |
|