S-Plastics ValoxEXVX1219resin PBT, Super High Flow, 20% diperkuat kaca, tahan hidrolik.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 109 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 109 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.5 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 8760 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 156 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6160 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 103 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 103 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6680 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 147 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5480 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 82 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 82 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 205 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/50 | 202 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 200 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 204 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.45 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 39 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.45 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 27 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:08/17/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 60 - 75 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:08/17/2006 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox EXVX1219.pdf |
|