S-Plastics ValoxVAC3001resin adalahPBT kosong dimodifikasi dengan elastomer.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 160 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 79 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2300 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 25 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 120 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 25 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 54 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 2 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 156 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 118 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 47 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.18E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.9E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 9.18E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.9E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 156 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 155 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 48 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 2.1 - 2.3 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 2.1 - 2.3 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/1,2 kgf | 17 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/1,2 kg | 16 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 0,8 mm | 15.9 | kV/mm | ASTM D 149 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 50 - 75 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox VAC3001.pdf |
|