S-Plastics ValoxEXVX0125resin adalah 30% PBT diisi kaca, Flame Retardant (UL94 V-0/5VA dinilai), Release Mold (Valox EXVX0125 akan menjadi Valox 420SE0 global grade pada tanggal 1 Januari 2009)
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 90 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 90 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 12000 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 186 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9800 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 119 | - | ASTM D 785 |
| Tekanan tarik, hasil, 5 mm/menit | 120 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 120 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.9 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 180 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 620 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 60 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 57 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 5 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 212 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 200 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.52E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 2.52E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 2.52E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 2.52E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 200 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.63 | - | ASTM D 792 |
| Volume Spesifik | 0.61 | cm3/g | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 1,5-3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2-4,6 mm | 0.6 - 1 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 42 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.62 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.07 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 29 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >3.4E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 19.2 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 24 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 3.8 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.7 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.002 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.71 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 2 | mm | UL 94 |
| Sinar UV, paparan air/pencelupan | F2 | - | UL 746C |
| Sumber GMD, terakhir diperbarui:09/09/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 255 - 275 | °C |
| Suhu Nozzle | 250 - 270 | °C |
| Suhu depan - Zona 3 | 255 - 275 | °C |
| Tengah - Zona 2 Suhu | 250 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 245 - 265 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:09/09/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox EXVX0125.pdf |
|