S-Plastics ValoxEXVX0025resin adalah 50% resin PBT-PET yang diperkuat Serat Kaca
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 175 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 175 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 17500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 255 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 16000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 40 | kJ/m2 | ISO 180/1U |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 1.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 210 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 206 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.76 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 7 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:09/04/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 270 - 300 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Sumber GMD, terakhir diperbarui:09/04/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox EXVX0025.pdf |
|