S-Plastics ValoxDR48Vresin adalah resin PBT injeksi yang diperkuat kaca 17% dan tahan api.Trimmer dan casing elektromotor.
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, pecah, 5 mm/menit | 110 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6500 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5500 | MPa | ISO 178 |
| Kekerasan, Rockwell R | 118 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 50 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.19 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 185 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 185 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 185 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.6 - 0.9 | % | Metode S-Plastics |
| Kepadatan | 1.51 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.17 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 12 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+13 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 1.8E+14 | Ohm | IEC 60093 |
| Kekuatan dielektrik, waktu pendek, 1,0 mm | 19 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 19 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.6 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3.4 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 175 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 150 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.89 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 31 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:12/22/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 240 - 260 | °C |
| Suhu depan - Zona 3 | 245 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:12/22/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox DR48V.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|