S-Plastics ValoxCS3002Uresin adalah Polyester tanpa isi, UV dan warna stabil, umum tujuan pelepasan kelas.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 88 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2420 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 48 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 183 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 58 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.33 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 1.7 - 2.3 | % | Metode S-Plastics |
| Sumber GMD, terakhir diperbarui:06/18/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Suhu Peleburan | 235 - 265 | °C |
| Suhu Cetakan | 45 - 60 | °C |
| Sumber GMD, terakhir diperbarui:06/18/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox CS3002U.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|