S-Plastics ValoxVX5530resin adalahcampuran PBT+PC yang tahan api, diperkuat serat kaca 15%, mineral 10%, dengan warp rendah yang sangat baik
karakteristik.
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 75 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, pecah, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7500 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6950 | MPa | ISO 178 |
| Kekerasan, H358/30 | 160 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 32 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 32 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 34 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 34 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 173 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 175 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 137 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 125 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 110 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 125 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.3 - 0.5 | % | Metode S-Plastics |
| Kepadatan | 1.57 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 30 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 2.5 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:09/02/1999 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 240 - 260 | °C |
| Suhu depan - Zona 3 | 245 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:09/02/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
SS-Plastics Valox VX5530.pdf |
|