S-Plastics ValoxVX5005resin adalahcampuran PBT+PC bertulang 5% diperkuat serat kaca dengan karakteristik warpage rendah.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 59 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 20 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2900 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2650 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 55 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 55 | kJ/m2 | ISO 180/1U |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 132 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 120 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 100 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.5 - 0.9 | % | Metode S-Plastics |
| Kepadatan | 1.32 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.19 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.11 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 8 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 14 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.009 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.004 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 200 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 100 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) ((4) | 1.6 | mm | UL 94 oleh GE |
| Glow Wire Flammability Index 750°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Glow Wire Flammability Index 850°C, melewati pada | 3 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 21 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui: 02/25/1993 | |||
| Suhu Pengeringan | 110 - 120 | °C | |
| Waktu Pengeringan | 2 - 4 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 250 - 270 | °C | |
| Suhu Nozzle | 240 - 260 | °C | |
| Suhu depan - Zona 3 | 245 - 265 | °C | |
| Tengah - Zona 2 Suhu | 240 - 255 | °C | |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C | |
| Suhu Hopper | 40 - 60 | °C | |
| Suhu Cetakan | 40 - 100 | °C | |
| Sumber GMD, terakhir diperbarui: 02/25/1993 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox VX5005.pdf |
|