SabikCycoloy CY5100resin adalahCampuran PC/ABS tahan api menggunakan sistem tahan api non-brominated dan non-chlorinated, menawarkan keseimbangan aliran / dampak yang sangat baik untuk aplikasi ukuran besar
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 47 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.1 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 65 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2760 | MPa | ASTM D 638 |
| Tekanan tarik, hasil, 50 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 46 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 35 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2750 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 94 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2440 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 400 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 80 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*3 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 104 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 106 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 88 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.6 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/2,16 kg | 23 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Resistivitas Volume | 1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 46 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 31 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.007 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-1 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 1,0 mm | 825 | °C | IEC 60695-2-13 |
| Suhu pembakaran kawat bercahaya, 2,0 mm | 825 | °C | IEC 60695-2-13 |
| Suhu pembakaran kawat bercahaya, 3,0 mm | 825 | °C | IEC 60695-2-13 |
| Indeks Oksigen (LOI) | 31 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:11/27/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 300 | °C |
| Suhu Nozzle | 250 - 300 | °C |
| Suhu depan - Zona 3 | 250 - 300 | °C |
| Tengah - Zona 2 Suhu | 240 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 85 | °C |
| Sumber GMD, terakhir diperbarui:11/27/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |