SabikCycoloy CX7259resin adalahadalah campuran polikarbonat bertekanan yang dimodifikasi tahan api yang ditujukan untuk desain dinding ultra tipis.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 80 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2630 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2620 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 64 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 49 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 70 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 98 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2670 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 127 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 69 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 70 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 9 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 101 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 93 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 101 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 104 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/2,16 kgf | 23 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.17 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/2,16 kg | 19 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 28 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-2 Flame Class Rating (3) | 0.3 | mm | UL 94 |
| UL diakui, 94V-1 Flame Class Rating (3) | 0.5 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.6 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:05/15/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 270 - 300 | °C |
| Suhu Nozzle | 265 - 300 | °C |
| Suhu depan - Zona 3 | 265 - 300 | °C |
| Tengah - Zona 2 Suhu | 260 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 300 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:05/15/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |