S-Plastics ValoxVIC4311resin adalahSebuah PBT 30 persen diisi kaca, dampak dimodifikasi dengan adhesi epoksi yang sangat baik.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 83 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 84 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 8360 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 129 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6080 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 86 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 84 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7370 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 139 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6180 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 137 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 97 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 13 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 9 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 16 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 180 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 220 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 205 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.14E-04 | 1/°C | ASTM E 831 |
| CTE, -30°C sampai 30°C | 3.E-05 | 1/°C | TMA |
| CTE, -40°C sampai 40°C, aliran | 2.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.14E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 175 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 170 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 175 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.42 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 6,4 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 19 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.42 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.09 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 15 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+16 | Ohm | ASTM D 257 |
| Permittivitas relatif, 50/60 Hz | 3 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:10/13/2004 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:10/13/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox VIC4311.pdf |
|