SabikCycoloy CS9610resin adalahcampuran FR PC/ABS menggunakan sistem tahan api non-brominated dan non-chlorinated, menawarkan optimum
Kelas ini berpotensi dapat dipertimbangkan untuk berbagai aplikasi di bidang seperti transportasi,peralatan elektronik konsumen dan peralatan listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 55 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2600 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 98 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2440 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 62 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 45 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 98 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 800 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 72 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*3 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 118 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 105 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/50 | 124 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 127 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 15 | g/10 menit | ASTM D 1238 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 12 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 2 | mm | UL 94 |
| Densitas asap, api, Dmax | 225 | - | ASTM E 662 |
| Densitas Asap, Api, Ds 1,5 menit | 40 | - | ASTM E 662 |
| Densitas Asap, Api, Ds 4 min | 150 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:10/15/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 270 - 300 | °C |
| Suhu Nozzle | 265 - 300 | °C |
| Suhu depan - Zona 3 | 265 - 300 | °C |
| Tengah - Zona 2 Suhu | 260 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 300 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:10/15/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |