SabikCycoloy CP8320resin adalahCycoloy Berkualitas Panas Rata-rata untuk Otomotif
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 45 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 40 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2100 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 70 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2000 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2100 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 600 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 400 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 55 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*3 +23°C | 60 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 30 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 30 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 106 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 90 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pergi | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 106 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 107 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.1 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 14 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.1 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.3 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 13 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 35 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 25 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | IEC 60243-1 |
| Sumber GMD, terakhir diperbarui:06/14/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 95 - 105 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 280 | °C |
| Suhu Nozzle | 230 - 270 | °C |
| Suhu depan - Zona 3 | 240 - 280 | °C |
| Tengah - Zona 2 Suhu | 240 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 250 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:06/14/2006 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy CP8320.pdf |
|