SabikCycoloy CM6140resin adalahcampuran PC/ABS tahan api yang diisi. Sistem FR non-brominated & non-chlorinated untuk memenuhi UL94
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3500 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 100 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3300 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 15 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 97 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3450 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 200 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 88 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 50 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*3 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 91 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 83 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 97 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 89 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 98 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 102 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.26 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.1 | % | ASTM D 570 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.01 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/2,16 kgf | 17.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.25 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.09 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.01 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 14 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 2.68E+16 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 3.54E+15 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-1 Flame Class Rating (3) | 0.6 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 0.8 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 1,0 mm | 850 | °C | IEC 60695-2-13 |
| Suhu pembakaran kawat bercahaya, 3,0 mm | 800 | °C | IEC 60695-2-13 |
| Sumber GMD, terakhir diperbarui:12/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 | °C |
| Waktu Pengeringan | >4 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 275 - 300 | °C |
| Suhu Nozzle | 280 - 300 | °C |
| Suhu depan - Zona 3 | 280 - 300 | °C |
| Tengah - Zona 2 Suhu | 275 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 300 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui:12/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy CM6140.pdf |
|