SabikCycoloy CE8510resin adalahKelas ekstrusi PC / ABS. viskositas rendah, dampak tinggi dan ductility.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 57 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2170 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2350 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2250 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 650 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 530 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 60 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*3 +23°C | 50 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 35 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 35 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 118 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 124 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 107 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 122 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.14 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 8.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.14 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.1 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 10 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:09/03/2004 | |||
| Parameter | ||
| Ekstrusi Film | Nilai | Satuan |
| Suhu Pengeringan | 90 - 110 | °C |
| Waktu Pengeringan | 4 | jam |
| Waktu pengeringan (kumulatif) | 6 - 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Barel - Belakang | 220 - 250 | °C |
| Suhu Barel - Rata-rata | 220 - 250 | °C |
| Suhu Barel - Depan | 220 - 250 | °C |
| Suhu mati | 220 - 250 | °C |
| Suhu gulungan | 200 - 250 | °C |
| Sumber GMD, terakhir diperbarui:09/03/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy CE8510.pdf |
|