SabikCycoloy CE1820resin adalahKelas Ekstrusi Sikloy, ABS + PC Campuran, CTE Rendah, Panas Tinggi, Dampak Tinggi, Kelas Thermoforming Ekstrusi
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 121 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 120 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3300 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2990 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 429 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 108 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 57 | J | ASTM D 3763 |
| Energi dampak instrumen @ puncak, -30 | 51 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 118 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 138 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 120 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, xflow | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 60°C, aliran | 6.6E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.1 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.4 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 230°C/3,8 kgf | 1.5 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 11 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:10/03/2003 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 225 - 240 | °C |
| Suhu Nozzle | 220 - 230 | °C |
| Suhu depan - Zona 3 | 220 - 230 | °C |
| Tengah - Zona 2 Suhu | 210 - 220 | °C |
| Bagian belakang - Zona 1 Suhu | 200 - 210 | °C |
| Suhu Cetakan | 70 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 230 - 270 | °C |
| Barel - Zona 1 Suhu | 215 - 255 | °C |
| Barel - Zona 2 Suhu | 220 - 260 | °C |
| Barel - Zona 3 Suhu | 225 - 270 | °C |
| Suhu adaptor | 240 - 270 | °C |
| Suhu mati | 240 - 270 | °C |
| Temperature Roll Stack - Atas | 70 - 95 | °C |
| Temperature Roll Stack - Pertengahan | 95 - 115 | °C |
| Roll Stack Temp - Bagian bawah | 105 - 130 | °C |
| Sumber GMD, terakhir diperbarui:10/03/2003 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy CE1820.pdf |
|
Dapatkan Kutipan Terbaru