S-Plastics ValoxV9260DCSresin adalahColor Stable Glass Filled PET (hanya untuk warna gelap)
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 155 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 155 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 210 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 230 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 235 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 230 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.56 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.27 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 14 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:06/29/2006 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox V9260DCS.pdf |
|