SabikCycoloy C8040RECresin adalahPC + ABS dengan 50% kandungan daur ulang. dirancang untuk pasar interior otomotif. memiliki dampak suhu rendah yang baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 54 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 90 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2340 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 87 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2300 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 90 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2250 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2220 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 670 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 480 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 54 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 61 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 57 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 43 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 -40°C | 49 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 68 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 122 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 126 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 111 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.2E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 122 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 127 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 107 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.14 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 12 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.13 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/09/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 275 - 300 | °C |
| Suhu Nozzle | 275 - 300 | °C |
| Suhu depan - Zona 3 | 260 - 300 | °C |
| Tengah - Zona 2 Suhu | 255 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 290 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:09/09/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy C8040REC.pdf |
|