S-Plastics ValoxV9235resin adalahValox terstabil panas, Kelas terisi kaca dengan pelepasan cetakan berdasarkan PET daur ulang.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 95 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 95 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 1.8 | % | ASTM D 638 |
| Tekanan tarik, putus | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6250 | MPa | ASTM D 638 |
| Tekanan tarik, hasil, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 50 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 50 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 19 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 19 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 3.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.4E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 230 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 230 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.32 - 0.4 | % | Metode S-Plastics |
| Kepadatan | 1.46 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.36 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.13 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 38 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:08/10/2005 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 130 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 270 - 290 | °C |
| Suhu Nozzle | 260 - 280 | °C |
| Suhu depan - Zona 3 | 270 - 290 | °C |
| Tengah - Zona 2 Suhu | 260 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 270 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 35 - 65 | °C |
| Sumber GMD, terakhir diperbarui:08/10/2005 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox V9235.pdf |
|