S-Plastics ValoxK4530resin adalah15% PBT diperkuat kaca, Stabil hidrolitik, Aliran tinggi, Konektor Otomotif.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 103 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 103 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4 | % ASTM D 638 | |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4 | % ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3550 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 150 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4640 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 400 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 58 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 218 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 193 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.41 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.7 - 0.9 | % Metode S-Plastics | |
| Penyusutan jamur, xflow, 3,2 mm | Satu, satu.2 | % Metode S-Plastics | |
| Setelah 40 Siklus, Mirip dengan USCAR-2, Kelas III | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 82 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.5 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4520 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 9.7 | % ASTM D 790 | |
| Dampak Instrumen, Total Energi, 23°C | 6 | J | ASTM D 3763 |
| Properti setelah 1008 jam di 125 °C | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 98 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4820 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 7 | % ASTM D 790 | |
| Dampak Instrumen, Total Energi, 23°C | 5 | J | ASTM D 3763 |
| Setelah 40 Siklus, Mirip dengan USCAR-2, Kelas IV | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 89 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.3 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5100 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 6 | % ASTM D 790 | |
| Dampak Instrumen, Total Energi, 23°C | 4 | J | ASTM D 3763 |
| Properti setelah 1008 jam di 155?C | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4812 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 97.2 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 0 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 3.8 | % | ASTM D 790 |
| Sumber GMD, terakhir diperbarui:03/25/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 60 - 75 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:03/25/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox K4530.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|