S-Plastics ValoxV8090resin adalah50% resin PBT-PET yang diperkuat dengan serat kaca
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 175 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 175 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 17500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 255 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 16000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 40 | kJ/m2 | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 1.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 210 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 206 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.76 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.16 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 7 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:05/21/2008 | |||
|