S-Plastics ValoxK3501resin adalahPBT yang tidak diisi, Stabil Hidrolitik, Stabil Panas, Modifikasi Dampak.Bertujuan untuk aplikasi mobil yang membutuhkan kelembaban/panas USCAR-2 Kelas III
kinerja.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 24 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 51 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2430 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 71 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2080 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 73 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.2 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 37 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2020 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 73 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2020 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir, -30°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 89 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, 0°C | 83 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -20°C | 73 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 48 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -40°C | 60 | J | ASTM D 3673 |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 127 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 46 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.7E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | NA | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 170 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 170 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 46 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 3,2 mm | 1.7 - 2.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 1.7 - 2.6 | % | Metode S-Plastics |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.34 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 26 | cm3/10 menit | ISO 1133 |
| Setelah 40 Siklus, Mirip dengan USCAR-2, Kelas III | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 37 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 12 | % | ASTM D 638 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2350 | MPa | ASTM D 790 |
| Dampak Instrumen, Total Energi, 23°C | 58 | J | ASTM D 3763 |
| Properti setelah 1008 jam di 125 °C | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 54 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 25 | % | ASTM D 638 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2330 | MPa | ASTM D 790 |
| Dampak Instrumen, Total Energi, 23°C | 61 | J | ASTM D 3763 |
| Sumber GMD, terakhir diperbarui:04/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 60 - 75 | °C |
| Waktu Pengeringan | 4 - 5 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:04/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox K3501.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|