S-Plastics ValoxK3500resin adalahPBT yang tidak diisi, dampaknya dimodifikasi, aliran tinggi, stabil secara hidrolisis.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % ASTM D 638 | |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 47 | % ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 1750 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 79 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2180 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 121 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 48 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.26 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 2.1 - 2.4 | % Metode S-Plastics | |
| Setelah 40 Siklus, Mirip dengan USCAR-2, Kelas III | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 17 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2040 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 13.1 | % ASTM D 790 | |
| Dampak Instrumen, Total Energi, 23°C | 48 | J | ASTM D 3763 |
| Properti setelah 1008 jam di 125 °C | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.8 | % ASTM D 638 | |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 14.7 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2280 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 8.8 | % ASTM D 790 | |
| Dampak Instrumen, Total Energi, 23°C | 17 | J | ASTM D 3763 |
| Setelah 40 Siklus, Mirip dengan USCAR-2, Kelas IV | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 17 | % ASTM D 638 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2280 | MPa | ASTM D 790 |
| Ketegangan lentur, 1,3 mm/menit, rentang 50 mm | 8.8 | % ASTM D 790 | |
| Dampak Instrumen, Total Energi, 23°C | 42 | J | ASTM D 3763 |
| Properti setelah 1008 jam di 155?C | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 2.5 | % ASTM D 638 | |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 37 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2716 | MPa | ASTM D 638 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 0 | MPa | ASTM D 790 |
| Sumber GMD, terakhir diperbarui:10/21/1998 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 95 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Suhu Nozzle | 240 - 255 | °C |
| Suhu depan - Zona 3 | 245 - 260 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 250 | °C |
| Suhu Cetakan | 50 - 75 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.025 | mm |
| Sumber GMD, terakhir diperbarui:10/21/1998 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox K3500.pdf |
|