S-Plastics ValoxV4860HRresin adalah30% PBT diperkuat kaca, UL94 V-0 dinilai, Stabil hidrolisis, Impact Modified.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 116 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 114 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9750 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 174 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 2 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6740 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 111 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 110 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.1 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9440 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 183 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 182 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 2.9 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7870 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 90 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 74 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 13 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 176 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 197 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 221 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 205 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 2.35E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 1.14E-04 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 2.28E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 1.19E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, perkiraan maksimum | 75 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 176 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 175 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 188 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.64 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.18 - 0.21 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.75 - 0.94 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 17.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.64 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.19 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 12 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 0.8 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:02/02/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 230 - 260 | °C |
| Suhu Nozzle | 240 - 260 | °C |
| Suhu depan - Zona 3 | 240 - 260 | °C |
| Tengah - Zona 2 Suhu | 230 - 250 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 240 | °C |
| Suhu Cetakan | 60 - 120 | °C |
| Tekanan Belakang | 5 - 10 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 30 - 70 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:02/02/2005 | ||
Produk jual panas (dalam persediaan)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT +kaca yang diisi: DR51, DR48, 420 420se0, 553, 508, 420HP
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Valox V4860HR.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|