S-Plastics ValoxV4030resin adalahPBT yang Dipenuhi Kaca dan Stabilisasi Panas
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5600 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 155 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pergi | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 200 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.41 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 12 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 1 | Kode PLC | UL 746A |
| Resistivitas Volume | 1.E+15 - 2.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 1.E+15 - 2.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 26 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 24 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.001 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.015 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 300 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Glow Wire Flammability Index 750°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:09/20/2007 | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5600 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 155 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pergi | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 200 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.41 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 12 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 1 | Kode PLC | UL 746A |
| Resistivitas Volume | 1.E+15 - 2.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 1.E+15 - 2.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 26 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 24 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.001 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.015 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 300 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Glow Wire Flammability Index 750°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:09/20/2007 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox V4030.pdf |
|
Dapatkan Kutipan Terbaru