S-Plastics ValoxIQNH4550resin adalah produk tahan api non-brominated/non-chlorinated berdasarkan Valox iQ yang ramah lingkungan*
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 104 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 104 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 11000 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 157 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9370 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10420 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 159 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9350 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 49 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 46 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 6 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 32 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 190 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 2.3E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 7.8E+01 | 1/°C | ASTM E 831 |
| CTE, -30°C sampai 80°C, aliran | 2.8E+01 | 1/°C | ISO 11359-2 |
| CTE, -30°C sampai 80°C, xflow | 1.05E+02 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 200 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.53 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.9 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.8 - 1.3 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 20 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.52 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.25 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 15 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan | 275 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 0.8 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 3,0 mm | 800 | °C | IEC 60695-2-13 |
| Sumber GMD, terakhir diperbarui:12/01/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Suhu Nozzle | 230 - 255 | °C |
| Suhu depan - Zona 3 | 240 - 260 | °C |
| Tengah - Zona 2 Suhu | 235 - 250 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 240 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:12/01/2008 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox IQNH4550.pdf |
|