S-Plastics Valox553resin adalah 30% GR PBT+PC, UL94 V-0. Mengurangi karakteristik warpage.Aplikasi; pemegang peralatan, lampu sorot, motor listrik, rumah pompa, dll.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 179 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6890 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 640 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 85 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 204 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 160 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.16E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 2.16E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 125 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 110 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 125 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.59 | - | ASTM D 792 |
| Volume Spesifik | 0.63 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.07 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 1,5-3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2-4,6 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 1,5-3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2-4,6 mm | 0.6 - 0.9 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 4.3E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 18.8 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 25.5 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 3.8 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.7 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.002 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 1 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.86 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 2.31 | mm | UL 94 |
| CSA (Lihat File untuk daftar lengkap) | LS88480 | File No. | CSA terdaftar |
| Indeks Oksigen (LOI) | 37.1 | % | ASTM D 2863 |
| Sinar UV, paparan air/pencelupan | F1 | - | UL 746C |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
Produk jual panas (dalam persediaan)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT +kaca yang diisi: DR51, DR48, 420 420se0, 553, 508, 420HP
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Valox 553.pdf |
|