S-Plastics ValoxV3500EXresin adalahPBT, Flame Retardant, Heat Stabilized, Extrusion grade untuk aplikasi monofilament/Fiber
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 80 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2900 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, aliran | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 180 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 180 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 62 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.45 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 13 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 0.8 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:11/03/2006 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox V3500EX.pdf |
|