S-Plastics Valox507resin
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 122 | MPa | Metode S-Plastics - Jepang |
| Tekanan tarik, putus | 3 - 3 | % | Metode S-Plastics - Jepang |
| Tekanan Fleksural | 183 | MPa | ASTM D 790 |
| Modulus Flexural | 8110 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 119 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 88 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 201 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 216 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C | 3.E-05 - 3.E-05 | 1/°C | TMA |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.51 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.06 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.1 - 0.2 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 6,4 mm | 0.3 - 0.6 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+16 | Ohm | ASTM D 257 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.83 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui: 02/03/2000 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox 507.pdf |
|