S-Plastics ValoxV3100HRresin adalahKetahanan hidrolitik kelas poliester viskositas rendah.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 50 | % | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 86 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2410 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 52 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 148 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, aliran | 1.19E-04 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Volume Spesifik | 0.1 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.06 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 2.1 - 2.3 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 2.2 - 2.4 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 2.5E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 16.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.88 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.001 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.016 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:02/11/2002 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox V3100HR.pdf |
|