S-Plastics ValoxV3001MCresin adalahResin injeksi PBT yang tidak diperkuat, langsung dapat dimetalisir dengan karakteristik aliran tinggi
| Mekanis | Nilai | Satuan | Standar | |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 | |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 17 | MPa | ASTM D 638 | |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 20 | % | ASTM D 638 | |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 2650 | MPa | ASTM D 638 | |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 89 | MPa | ASTM D 790 | |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2410 | MPa | ASTM D 790 | |
| Tekanan tarik, hasil, 50 mm/menit | 59 | MPa | ISO 527 | |
| Tekanan tarik, pecah, 50 mm/menit | 53 | MPa | ISO 527 | |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 | |
| Tekanan tarik, putus, 50 mm/menit | 15 | % | ISO 527 | |
| Modulus tarik, 1 mm/menit | 2700 | MPa | ISO 527 | |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 | |
| Kekerasan, H358/30 | 85 | MPa | ISO 2039-1 | |
| Kekerasan, Rockwell R | 117 | - | ISO 2039-2 | |
| Dampak | Nilai | Satuan | Standar | |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 | |
| Izod Dampak, bertanduk, -40°C | 58 | J/m | ASTM D 256 | |
| Energi Total Dampak Instrumen, 23°C | 56 | J | ASTM D 3763 | |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A | |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA | |
| Charpy Impact, bertanduk, 23°C | 3 | kJ/m2 | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
| Termal | Nilai | Satuan | Standar | |
| Vicat Softening Temperature, Tingkat B/50 | 185 | °C | ASTM D 1525 | |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 153 | °C | ASTM D 648 | |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 55 | °C | ASTM D 648 | |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 173 | °C | ASTM D 648 | |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 55 | °C | ASTM D 648 | |
| Konduktivitas Termal | 0.16 | W/m-°C | ISO 8302 | |
| CTE, 23°C sampai 80°C, aliran | 1.3E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C sampai 80°C, xflow | 1.3E-04 | 1/°C | ISO 11359-2 | |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 | |
| Vicat Softening Temperature, Tingkat B/50 | 185 | °C | ISO 306 | |
| Vicat Softening Temperature, Tingkat B/120 | 185 | °C | ISO 306 | |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 160 | °C | ISO 75/Be | |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 55 | °C | ISO 75/Ae | |
| FISIK | Nilai | Satuan | Standar | |
| Gravitasi Spesifik | 1.32 | - | ASTM D 792 | |
| Penyerapan air, 24 jam | 0.08 | % | ASTM D 570 | |
| Absorpsi air, (23°C/sat) | 0.34 | % | ASTM D 570 | |
| Penyusutan jamur, aliran, 3,2 mm | 1.8 - 2.1 | % | Metode S-Plastics | |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 33 | g/10 menit | ASTM D 1238 | |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 | |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 30 | cm3/10 menit | ISO 1133 | |
| Listrik | Nilai | Satuan | Standar | |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 | |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 | |
| Permittivitas relatif, 50/60 Hz | 3.3 | - | IEC 60250 | |
| Permittivitas Relatif, 1 MHz | 3.1 | - | IEC 60250 | |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 | |
| Faktor Dissipasi, 1 MHz | 0.02 | - | IEC 60250 | |
| Indeks Pelacakan Perbandingan | 600 | V | IEC 60112 | |
| Karakteristik Api | Nilai | Satuan | Standar | |
| Indeks Oksigen (LOI) | 20 | % | ISO 4589 | |
| Sumber GMD, terakhir diperbarui:10/23/2002 | ||||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox V3001MC.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|