S-Plastics ValoxV2015Uresin adalahPBT yang tidak diperkuat, tahan aus, UV Stabilized dirancang untuk aplikasi luar ruangan, pertanian, industri dan otomotif.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 39 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 17 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 300 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2500 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 65 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2060 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 52 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 230 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2540 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 62 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1870 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 1160 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 150 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 63 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -40°C | 75 | J | ASTM D 3673 |
| Izod Impact, bernotas 80*10*4 +23°C | 98 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 90 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 158 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 49 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.2E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 158 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 158 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 47 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 2.9 - 3.4 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 2.5 - 3 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 266°C/5,0 kgf | 9.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.34 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/25/2007 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |